H201 Water-based silver powder paint
Technical parameters
Drying time (25℃) Surface dry 0.5hours
Hands-on 24 hours
Drying 1 hour (60-80°C)
Complete factorization 7 days
Film hardness H
Paint film adhesion
Paint film flexibility
Impact resistance of paint film 50cm-kg
The special new port is always in the question, cloud ion water, water-based auxiliary M, high performance wrapping, and environmentally friendly filler on the customer group. It does not kill home, benzene, xylene and other organic solvents. Benzene, xylene and other organic solvents.Made of special water-based resin, imported water-based silver paste, functional additives and other materials, refined by advanced technology, it has the characteristics of high hardness of paint film, good weather resistance, excellent adhesion to different metal base materials, and good adhesion to primer.
Artificial ageing resistance 500h -
Inorganic high temperature resistant water paint/Composite high temperature resistant water paint
This product is a water-based inorganic heat-resistant coating, the base material and filler are composed of hot, non-combustible inorganic substances. The base material contains a large number of OH active groups, which react quickly with the active components in the filler and the active surface of steel to generate inorganic polymers with three-dimensional structure. The coating is integrated with the steel matrix to form a heat-resistant and anti-corrosion coating with electrochemical protection and physical shielding. It is especially suitable for the long-term protection of steel structures working in high temperature and corrosive environment.
Details
Technical parameter
Project index
Film color and appearance White, light green, grey, smooth
Specific gravity 2.0-2.3g/ml
Volume solid content 75%
Adhesion level 1
Hardness H ≥6H
Linear expansion coefficient 6.5x10-6/℃
Drying time (25+1℃)h:table dry ≤2: dry ≤48
Theoretical coating rate film thickness 75ρm; 2.5 m2/kg
colour ：Black (works best), brown, gray -
H2001 Waterborne polyurethane hammertone paint
The special imported water-based trapezium, the national chemical science, deionized water, water-based additives and environmental protection filler and other components, does not contain benzene, a family, second-grade benzene and other organic solvents.The product is prepared by using water-based aliphatic polyurethane resin as film forming base material, HDI as curing agent, adding environmentally friendly fillers and functional auxiliars. Full film, high gloss, bright color. Good adhesion, high hardness, excellent weather resistance.
Technical parameters
Drying time (25℃℃) Surface dry 1 hour
Hands-on 24 hours
dryer
Fully Factorized 7 days 1 hour (60-80°C)
Gloss ≥80%
Varnish hardness
Paint film adhesion
Paint film flexibility
1mm
Paint film impact resistance
Resistant to artificial ageing 50cn, kg
Mixing ratio 20:3 (weight ratio)
Mixing method: Mix component A thoroughly, add component B and continue to mix until uniform.
Theoretical dosage 4-tmi/(60-80μm)
Boiling period (25℃℃) 5-10min
Suitable period (25°C) 2h -
Waterborne Amino-Acrylic Baking Enamel
Appearance:Light yellow liquid With eyes
Solid content：76±2% 30min@120℃
Water dilution：Infinite Dilution ----
Hydroxyl value：115 mgKOH/g
For solid resin, theoretical value
Viscosity (Brookfield 25℃)*：30-70mpa.s
NDJ-79 Rotational Viscometer
Density：1.142 g/cm3 Densitym meter
Paint film color and appearance: in line with the standard template and color difference range, smooth and smooth
Film thickness um: 20-30 GB/T 1724-79(89)
Gloss: Agreed GB/T 1724-79(89)
Hardness: ≥2H GB/T 6739
Impact: 50kg·cm GB/T 1732-79(93)
Flexibility mm:1 GB/T 1732-79(93)
Adhesion:Level 1 GB1720-79(89)
Water resistance:72h, no foaming, no shedding GB/T 1733-93
Packing: Net weight 25Kg/ barrel, 200kg/ barrel