H604 Waterborne epoxy ferro-iron intermediate paint
Color: gray
Solid content: 60±2%
Mitsuze: No light
Drying time (25 ° C) : table dry for 1 hour
24 hours of hard work
Fully cured for 7 days
Drying (70-80℃) : 2 hours of work
Film hardness
Film adhesion: 1 level
Film flexibility: 2mm
Film impact resistance: 50cm.kg
Theoretical coating rate: 8m'/kg (dry film 40μm)
Construction method: Ratio A component: B component = 9:1
Construction method: air spraying/airless spraying
Diluent: clean water
Dilution: 5-15%
Nozzle diameter: 1.5-2.5mm
Spraying pressure: 0.4-0.6Mpa
Application period: 3h "Under the condition of 20℃)
Coating matching: Select matching system according to requirements.
This product is not recommended for use alone, and can be used in conjunction with most of our water-based or solvent-based primers and topcoats.
Packing specification: A component: 18kg/ barrel B component: 2kg/ barrel
The construction environment and other explanatory data are the same as "H602 water-based epoxy primer", please refer to. -
Waterborne single component varnishes
1.Single-component, waterborne, polyurethane finish for wood or cork floors, destined for residential/commercial use.
2.For further enhance these features you can add 10% IDRO2 hardener to the paint.
3.The product, catalyzed with IDRO2, is also particularly suited for parquet floors in gymnasiums, because it amply fulfils standard requirements with regard to slipperiness EN 13036-4. Designed for ease of application, the product can be applied by roller, brush or spraying and it is particularly suitable for light wood species (oak, beech, pine, etc.).
Semigloss sheen (about 50 gloss)
Satin sheen (about 35 gloss)
Mat sheen (about 10 gloss)
Packaging: 1L; 5L; 10L -
H201 Water-based silver powder paint
Technical parameters
Drying time (25℃) Surface dry 0.5hours
Hands-on 24 hours
Drying 1 hour (60-80°C)
Complete factorization 7 days
Film hardness H
Paint film adhesion
Paint film flexibility
Impact resistance of paint film 50cm-kg
The special new port is always in the question, cloud ion water, water-based auxiliary M, high performance wrapping, and environmentally friendly filler on the customer group. It does not kill home, benzene, xylene and other organic solvents. Benzene, xylene and other organic solvents.Made of special water-based resin, imported water-based silver paste, functional additives and other materials, refined by advanced technology, it has the characteristics of high hardness of paint film, good weather resistance, excellent adhesion to different metal base materials, and good adhesion to primer.
Artificial ageing resistance 500h -
Inorganic high temperature resistant water paint/Composite high temperature resistant water paint
This product is a water-based inorganic heat-resistant coating, the base material and filler are composed of hot, non-combustible inorganic substances. The base material contains a large number of OH active groups, which react quickly with the active components in the filler and the active surface of steel to generate inorganic polymers with three-dimensional structure. The coating is integrated with the steel matrix to form a heat-resistant and anti-corrosion coating with electrochemical protection and physical shielding. It is especially suitable for the long-term protection of steel structures working in high temperature and corrosive environment.
Details
Technical parameter
Project index
Film color and appearance White, light green, grey, smooth
Specific gravity 2.0-2.3g/ml
Volume solid content 75%
Adhesion level 1
Hardness H ≥6H
Linear expansion coefficient 6.5x10-6/℃
Drying time (25+1℃)h:table dry ≤2: dry ≤48
Theoretical coating rate film thickness 75ρm; 2.5 m2/kg
colour ：Black (works best), brown, gray -
H2001 Waterborne polyurethane hammertone paint
The special imported water-based trapezium, the national chemical science, deionized water, water-based additives and environmental protection filler and other components, does not contain benzene, a family, second-grade benzene and other organic solvents.The product is prepared by using water-based aliphatic polyurethane resin as film forming base material, HDI as curing agent, adding environmentally friendly fillers and functional auxiliars. Full film, high gloss, bright color. Good adhesion, high hardness, excellent weather resistance.
Technical parameters
Drying time (25℃℃) Surface dry 1 hour
Hands-on 24 hours
dryer
Fully Factorized 7 days 1 hour (60-80°C)
Gloss ≥80%
Varnish hardness
Paint film adhesion
Paint film flexibility
1mm
Paint film impact resistance
Resistant to artificial ageing 50cn, kg
Mixing ratio 20:3 (weight ratio)
Mixing method: Mix component A thoroughly, add component B and continue to mix until uniform.
Theoretical dosage 4-tmi/(60-80μm)
Boiling period (25℃℃) 5-10min
Suitable period (25°C) 2h -
Waterborne Amino-Acrylic Baking Enamel
Appearance:Light yellow liquid With eyes
Solid content：76±2% 30min@120℃
Water dilution：Infinite Dilution ----
Hydroxyl value：115 mgKOH/g
For solid resin, theoretical value
Viscosity (Brookfield 25℃)*：30-70mpa.s
NDJ-79 Rotational Viscometer
Density：1.142 g/cm3 Densitym meter
Paint film color and appearance: in line with the standard template and color difference range, smooth and smooth
Film thickness um: 20-30 GB/T 1724-79(89)
Gloss: Agreed GB/T 1724-79(89)
Hardness: ≥2H GB/T 6739
Impact: 50kg·cm GB/T 1732-79(93)
Flexibility mm:1 GB/T 1732-79(93)
Adhesion:Level 1 GB1720-79(89)
Water resistance:72h, no foaming, no shedding GB/T 1733-93
Packing: Net weight 25Kg/ barrel, 200kg/ barrel -
H602 Waterborne epoxy primer
Two-component water-based epoxy paint.This product is made of water-based ring carrier nozzle, water-based additives, environmentally friendly antirust filler, water-based epoxy coating agent, deionized water, etc. by special process, A, B two-component independent packaging.Waterborne Epoxy Primer is a two-component, low VOC, HAP-free, fast curing water-based epoxy primer coating. It has been engineered to provide excellent adhesion for Chemsol Non-Slip products.It is suitable for use on flooring, ramps, steps, and other areas where priming is recommended prior to application of Chemsol Non-Slip or other topcoats. It is suitable for industrial, commercial, marine, and consumer environments. It is easy to apply and has very little odor which makes it ideal for use in odor-sensitive areas both indoor and outdoor. It is designed to adhere to a variety of porous surfaces including concrete, wood, tile (prepared to expose porosity of the tile) and other surfaces. Priming is recommended for best performance of topcoats.Waterborne Epoxy Primer has been formulated to meet the strict requirements of South Coast Air Quality Management District Rule 1113. -
Special texture powder coating powder paint/Alkyd dip coating special paint/Waterborne fast drying dip paint
Quick Details
CAS No.:25135-73-3
Other Names:paint coating
MF:C22H26O10
EINECS No.:203-652-6
Place of Origin:Fujian, China
Main Raw Material:Resin
Usage:Appliance Paint, Building Coating, Car Paint, Furniture Paint
Application Method:Spray
State:Powder Coating
Brand Name:KINDA
Model Number:EP9807
Shape:Powder
Color:Customized Colors
MOQ:100kgs
Gross weight:20kg
Supply Ability:300 Ton/Tons per Month
Packaging Details:PE Bags, Cartons and Pallets
Carton Size:30*25*30cm
N.W: 19KG
G.W: 20KG
50cartons/Pallet
18tons/20ft
Port:Fuzhou Port,China